Following sound practice and complying with applicable standards is relatively straightforward and will greatly contribute to true and accurate results. Foremost to any Rockwell test process is identification of the proper hardness scale to be used on the component to be tested. There are 30 different Rockwell scales with the majority of applications covered by the Rockwell HRC and HRB scales for testing most steels, brass, and other metals. With the increasing use of materials other than common steel and brass, as well as requirements to test thin materials and sheet steel, a basic knowledge of the factors that must be considered in choosing the correct scale to ensure an accurate Rockwell test in necessary. The choice is not only between the regular hardness test and superficial hardness test, with three different major loads for each, but also between the diamond indenter and the 1/16, 1/8, 1/4 and 1/2 in. diameter steel ball indenters. Often an engineering specification is established at the material design phase and the operator can rely on documented scale requirements. If no specification exists or there is doubt about the suitability of a predetermined scale, an analysis should be made of the following factors that control scale selection:
AJR supply professional and honest service.
Material Type
In the absence of a specified hardness scale the material type should be identified and compared with various tables that list the typical type of scale that is applicable to a given material. Usually this is based on historical data and empirical testing information. As a rule of thumb, using the heaviest load that the material can withstand is advisable as the larger indent will provide the greatest integrity and be minimally affected by material surface condition. Typically, diamond scale indenters are used on hardened steels and other very hard materials while the ball scales are more applicable to the brass, copper alloy, aluminum type of materials. While material composition knowledge is a necessary tool in scale selection, there are several other extremely significant material parameters that come into play in determining the proper test meth and technique to be followed.
Material Thickness
Of primary importance in scale selection is the material thickness. Since the 30 Rockwell scales are distinguished by total test force, as well as the indenter type, a load or force that is excessive for the material thickness will be ultimately influence by the support anvil. Interruption in material flow such as this can will result in erroneous readings and significant misinterpretation of the actual material hardness. ASTM provides scale thickness requirements both in tabular as well as graphical form. It is recommended that these are used as a reference guide in deciding suitable scale based on material thickness. A general, albeit approximate only, rule is that the material should be a minimum of 10 times the depth of the indentation when using a diamond type indenter and at least 15 times the depth when using a ball type indenter. If necessary the actual depth of any indentation can be calculated to confirm this requirement is being met, but this is generally not necessary as the reference tables and graphs provide adequate information to make an educated decision. As a final rule, no deformation of the material should be evident on the supporting (underside) surface of the material.
Support
Specimen support is also extremely critical in Rockwell testing due to the fact that the method involves depth measurement. Any specimen movement is transferred to the indenter and the measurement system, resulting in an error being introduced into the test. With the precise nature of the test (keeping in mind that one Rockwell point on the regular scale equals 0.002 mm or 0. of an inch) a movement of only 0.001 of an inch could cause an error of over 10 Rockwell points. The supporting anvil should be selected to match the specimen geometry and to provide full and uncompromised support and it is essential that the anvil is rigid enough to prevent any deformation during use. There are certain criteria that must be met on all anvils; a good reference is ASTM E18 where basic guidelines can be found including anvil hardness recommendations. The supporting shoulder and the surface that the specimen sits on must be parallel to each other, and the anvil must present the test specimen perpendicular to the indenter. Both the supporting surface and the shoulder must be free of nicks, scratches and dirt, and be of sufficient design to properly support the material under test. Anvils should be checked on a regular basis, typically prior to each use, and if found too compromised they should be replaced. Damaged, nicked or dirty indenters can cause considerable drift and repeatability problems in hardness readings. A variety of standardized, as well as custom made fixtures, exist to accommodate the various specimen geometries that are tested. Some of the more common anvils include plane or flat anvils for supporting flat surfaces, the &#;V&#; style anvil for supporting cylindrical work, and the cylindron anvil for larger diameter parts. Another commonly used anvil is the pedestal spot anvil that has a small raised flat spot and is used when checking small, thin or irregularly shaped pieces as well as test materials not having a truly flat bottom. As it is essential that contact is made between the piece being tested and the part of the anvil immediately beneath the indenter, the small raised spot minimizes the effect that could be realized with non-flat test pieces by reducing the surface area of contact. Test pieces that are not flat should be placed on the spot anvil with the curved side down to ensure that solid contact is made with the anvil at the point of test. For support of thin sheet type product the diamond spot anvil is recommended, this anvil consists of a slightly raised, flat, polished diamond surface that supports the test piece and prevents damage and influence that might occur with a standard anvil. This anvil is only used with the 15 T or 30 T Rockwell scales. Using a diamond indenter with a diamond spot anvil is never recommended, as breakage of both the indenter and anvil is possible. The gooseneck anvil is recommended for testing outside diameter surfaces of thin walled tubing. It typically threads onto the tester lead screw or support holder and includes a mandrel at the top to support the part to be tested is placed over this mandrel to prevent material compliance during testing. Larger parts can be supported using large diameter test tables or a &#;T&#; slot style table that can be used to clamp the test piece to the table. Due to the size and weight of the &#;T&#; slot table they can only be used with Rockwell® testers that actuate the indenter down to the stationary table that&#;s affixed to the base of the tester as opposed to introducing the part to the diamond via lead screw actuation. Another useful fixture is the Vari-Rest fixture that extends horizontally to support elongated pieces.
Perpendicularity
It is a fundamental requirement that the surface to be indented is perpendicular to the direction of travel of the indenter and that the test piece does not move or slip during the test cycle. A study showed that the effect on the HRC scale indicated a tilt angle of one degree between the specimen surface and the axis of the indenter could result in a 5% error in hardness. Tilt angle should never exceed 2 degrees to ensure accurate testing. The perpendicularity of the indenter to the specimen is influenced by many factors, including the opposing surfaces of the material, the supporting anvil, and the mechanical components in the tester. In addition, the indenter and indenter holder plays a crucial role in perpendicularity.
Indent Spacing
During specimen testing or coupon block verification, the spacing between indents, as well as from the material edge, must be properly maintained to prevent any adjacent indents or worked edge from influencing the next test. The accepted criteria is that the distance from the center of any indentation shall be at least three times the diameter of the indentation In regards to distance from material edge, the distance from the center of any indentation to the edge of the test piece shall be at least two and one-half times the diameter of the indentation. The purpose for these distances is to ensure that any indentation made is not influenced by work hardening and flow of material around the previous indentation. Also, the edge distance requirement ensures that the indentation&#;s area of contact permits proper support.
Cylindrical Testing and Correction Factors
When testing on cylindrical surfaces the results will usually show a lower hardness value than if the material was flat. This condition is due to the curvature of the test piece and is dependent upon the applied force; the hardness of the material; the size and shape of the indentation; and the diameter of the test piece. If testing is to be used for control purposes only and all other factors are kept equal, (specimen diameter, scale and indenter), there will be sufficient information so that comparative data and subsequent testing is benchmarked. However, in most cases, it is better to compare the hardness of the rounded material with the hardness value of a flat piece, making correction factors necessary. In a cylindrical piece, the reduction in lateral support will result in the indenter penetrating further into the material which translates to lower hardness readings. If the diameter of the material is greater than 25 mm (1 inch) the surface will provide suitable surface structure for testing and corrections are not required. Lower diameter materials will need the correction factor added to the test result. Most digital Rockwell testers available provide the means to meet the cylindrical diameter and the correction factor will automatically be added to the result. In manual dial gage testers ASTM correction tables must be referenced to determine the correct factor to adjust by. Alternatively, and in contrast to convex surfaces, concave surfaces will provide higher material support due to the curvature towards the indenter and result in apparently harder material due to production of a shallower indent. In this case a correction factor must be subtracted. It should be noted that all corrections produce approximate results and should not be expected to meet exact specification. Also, it is critical to ensure the exact alignment of the indenter to the radius when cylindrical testing.
Surface Finish
As good practice, the material tested should be clean, smooth, and even. The degree of specimen surface roughness that can affect the hardness results is dependent on the Rockwell scale being used. Usually, the regular scales can tolerate a finished ground surface to obtain accurate results. However, as the applied forces get lighter, the surface&#;s requirements become more influential and the need for a smoother surface becomes more important. For the lowest hardness test force, the 15 Kgf scales, a polished or lapped surface is recommended. Care should be taken when finishing any material prior to testing to avoid the possibility of causing a work hardened condition to the material.
-01-06
Hardness is a critical property of materials, influencing their durability, wear resistance, and suitability for various applications. Industries rely on the Rockwell Hardness Tester to determine the hardness of a material accurately.
Developed by Stanley P. Rockwell in the early 20th century, this testing method became a key hardness test in the industry. However, this blog post explores the reasons why the Rockwell Hardness Test is the most common hardness tester in industry. Also, we will explore its significance in ensuring product reliability.
Reasons Rockwell hardness tester is common in different industries.
Let's have a look at the key reasons behind the popularity of Rockwell hardness tester in the industry:
Simplicity and Versatility of Rockwell hardness tester
One of the main reasons for the popularity of the Rockwell Hardness Test is its simplicity and versatility. The Rockwell hardness tester is relatively easy to use, making it accessible for both skilled technicians and novices.
The Rockwell method can evaluate the hardness of a diverse range of materials with a wide range of test scales available. It includes metals, plastics, and composites.
Its adaptability makes it an ideal choice for various industries, from automotive and aerospace to construction and manufacturing.
Non-destructive Testing Method
Unlike other hardness testing methods that require destructive sampling, the Rockwell Test allows for non-destructive testing.
Hardness tester uses a diamond cone or a hardened steel ball to make small indentations on the surface of materials.
It will help in measuring the resulting dept. This non-destructive nature of Rockwell enables manufacturers to assess the hardness of finished products without compromising their functionality or integrity.
Quality control and material selection For more information, please visit Digital Rockwell Hardness Testing Machine.
The Rockwell Hardness Test serves as a vital tool for quality control in industries that require precise material assessment.
Manufacturers can verify if they meet the desired specifications and standards by measuring the hardness of materials. This information helps in material selection, ensuring the selection of right materials for specific applications.
Time Efficiency
In fast-paced industrial environments, time is of the essence. The Rockwell Hardness Test offers significant time efficiency, allowing for rapid hardness measurements.
You can complete this hardness test within seconds, making it an invaluable tool for quality control during mass production processes. Manufacturers can quickly assess the hardness of materials and identify any potential deviations from desired specifications with minimal downtime.
Accuracy of Rockwell Hardness Tester
The Rockwell Hardness Test has undergone extensive standardization. Therefore, it ensures consistent and accurate measurements across different laboratories and industries.
Organizations have defined the test procedure, calibration, and specifications properly. These standardized guidelines provide a reliable framework for comparing hardness values, facilitating effective quality control and material selection.
Applicability to Different Hardness Ranges
The Rockwell Test method offers a wide range of test scales, ranging from superficial to regular scales. Superficial scales are used for testing materials with thin cross-sections or surfaces. In contrast, regular scales are suitable for bulkier materials.
Due to its versatility, the hardness tester is suitable to use to various hardness ranges. It helps in ensuring accurate measurements for materials with different properties and thicknesses.
Cost-Effectiveness of Rockwell Hardness Test.
For the simplicity and speed of the Rockwell Test, it is a cost-effective solution for hardness evaluation.
The equipment requirement for this test is relatively affordable than other hardness testing methods. Additionally, the non-destructive nature of the test eliminates the need for costly material samples or repeated testing. It will further help in reducing expenses for manufacturers.
Industry applications of Rockwell hardness tester.
The Rockwell Hardness Test is widely used in various industries due to its simplicity, versatility, and cost-effectiveness. Here are some of the key applications and significance of this testing method:
· The Rockwell Hardness Test is extensively used in the metals industry to assess the hardness of metallic materials. It helps determine the material's resistance to indentation, which correlates with its strength, wear resistance, and other mechanical properties.
· The Rockwell Test is also applicable to plastics, allowing manufacturers to evaluate the hardness of plastic materials. It is essential in industries where plastics are used, such as automotive, electronics, and consumer goods. It helps ensure the suitability and durability of plastic components.
Get the best iRock Digital Rockwell Hardness Tester from Sinowon.
Are you looking for a digital, semi-automatic Rockwell hardness tester? This iRock digital Rockwell tester is a suitable solution for you. It features automatic loading, unloading and conversion. The friendly computer and human interaction ensure its simplicity. The large LCD will help you to see details like indentation type, conversion value, and more within no time.
Conclusion
The Rockwell Hardness Test has become an integral part of industrial quality assurance due to its simplicity, versatility, non-destructive nature, time efficiency, standardization, and cost-effectiveness. By accurately assessing the hardness of materials, manufacturers can ensure the reliability and durability of their products. As industries continue to evolve, the Rockwell Test will likely remain a trusted method for hardness evaluation, contributing to the production of high-quality materials that meet the demands of modern applications.
Are you interested in learning more about Digital Vickers Hardness Tester? Contact us today to secure an expert consultation!